PostPosted: 23 Sep 2020, 09:39 
Offline
Manufacturer: RE-IMPACT

Joined: 01 Dec 2011, 06:01
Posts: 202
Location: Lembruch Dumber lake, Diepholz, Lower Saxony, Germany
Has thanked: 0 time
Been thanked: 25 times
Why should you primarily use black material coverings on Rendler woods

Red pimples are not so good for my tension-filled developments because they can store less heat, but simply reflect it..

Furthermore red pimples without sponge can make the dark top layer shine through, which is illegal in the ITTF rules interpretation, because the red rubbers can become darker in colour when pimples without sponge are used.

However, I would like to achieve that the heat is absorbed 100% by the surface wood, because the electromagnetic waves are reflected back by a light surface.

When these electromagnetic waves are absorbed, they are stored by the surface and converted into heat energy. All the more logical it is to use black pimples as material for my clubs to concentrate the static heat energy even more.

Because of these development reasons I like to work with dark wood layers, black burls can be used for better results, because darker woods and dark rubbers can absorb a lot of heat. Black rubbers contain more carbon fibres than red rubbers, making them softer than red rubbers.

According to the law of heat of unequal bodies I create the advantages of a high concentration of heat energy in the material, which can also release a great spin potential by high adhesive friction of the table tennis balls, which in turn can cause a very good cut reversal in material players.

However, it is essential to make it dependent on the players who can use a good technique.

If the face veneers also have very light wood surfaces between the interferences, the heat is reflected there more quickly s
will be.

In a stress-free wood material it is exactly the opposite. In order to make the material more disturbing, red rubbers are used here, as the black rubbers are used rather for the thick rubbers, in order to achieve better ball control on the tension-free woods.

_________________
Re-Impact GmbH. 49448 Lemförde "21 years of Rendler woods".
since November 1999 from A. RendlerGbR to Re-Impact GmbH
Phone +495443-9209999 mailto://[email protected]/ http://www.re-impact.de/


Top
 Profile  
 


PostPosted: 29 Sep 2020, 21:19 
Offline
Dark Knight
Dark Knight
User avatar

Joined: 13 Dec 2006, 12:34
Posts: 32659
Location: Adelaide, AU
Has thanked: 2041 times
Been thanked: 1344 times
Blade: Trinity Carbon
FH: Victas VS > 401
BH: Dr N Troublemaker OX
Thanks Achim, very interesting information. :up:

_________________
OOAK Table Tennis Shop | Re-Impact Blades | Butterfly Table Tennis bats
Setup1: Re-Impact Smart, Viper OX, Victas VS 401 Setup2: Re-Impact Barath, Dtecs OX, TSP Triple Spin Chop 1.0mm Setup3: Re-Impact Dark Knight, Hellfire OX, 999 Turbo
Recent Articles: Butterfly Tenergy Alternatives | Tenergy Rubbers Compared | Re-Impact User Guide


Top
 Profile  
 
Display posts from previous:  Sort by  
Post new topic Reply to topic  [ 2 posts ] 


Don't want to see this advertisement? Become a member and login, and you'll never see an ad again!



All times are UTC + 9:30 hours


Who is online

Users browsing this forum: lasta, Turtle_shell_wok and 28 guests


You cannot post new topics in this forum
You cannot reply to topics in this forum
You cannot edit your posts in this forum
You cannot delete your posts in this forum
You cannot post attachments in this forum

Search for:
Jump to:  
Copyright 2018 OOAK Table Tennis Forum. The information on this site cannot be reused without written permission.

Powered by phpBB® Forum Software © phpBB Group